For Use at Low-temperature
When utilizing conveyor chains at low-temperature such as within a fridge or within a cold atmosphere, the following circumstances may happen.
one) Very low temperature brittleness
Usually, a materials is embrittled at low-temperature and shock resistance is lowered. This phenomenon is called low-temperature brittleness, plus the degree of embrittlement differs from material to material.
The service limit of the conveyor chain depends on its specs.
2)Influence of freezing
At low-temperature, bending failure, roller rotation failure, fixing of chain, etc. could be brought on by the freezing of penetrated water or deposited frost inside the clearance amongst pins and bushings, bushings and rollers or inner plates and outer plates. These circumstances trigger an overload to act over the chain and drive, diminishing the existence from the chain.
To avoid freezing, usually, it’s proposed to fill the clearances having a low-temperature lubricant ideal to your services temperature to prevent water, frost, etc. from penetrating the respective portions of the chain. For lubrication, a silicon primarily based grease is advised.
For Use at High-temperature
Chains power is diminished by high-temperature atmosphere, direct conveying of high-temperature loads, or radiated heat, and so forth. 
The support restrict at high-temperature depends not over the temperature of the service setting however the temperature and materials of the chain body.
Following problems may perhaps happen when chains are utilised at high-temperature:
1) High temperature brittleness and fracture by lowered hardness of heat taken care of materials
2) Brittleness triggered by carbide precipitation
three) Abnormal put on by scale
four) Fatigue fracture brought on by repeated thermal shock (cooling and expansion)
5) Abnormal dress in due to an increase inside the coefficient of friction
6) Creep fracture
seven) Fracture as a result of thermal fatigue of welded place
8) Effects caused by thermal growth
?Stiff hyperlinks and rotation failure as a result of decreased clearance ?Fatigue fracture resulting from lowered fitting force
9）Lubrication failure and stiff hyperlinks as a result of deterioration and carbonization of lubricating oil
Grease great in heat resistance involve these determined by silicon, graphite or molybdenum disulfide.
For use at high-temperature, high-temperature resistance bearings and stainless steel bearings are suggested.